VT-42 CCL/Laminate VT-42 PP/Prepreg (Standard FR4 Material)

UL Approval: E214381 Version: Rev. B4 17/12/2017 /21

Storage Condition & Shelf Life

Precautions In Handling

  • The prepreg exceeding shelf time should be retested.
  • Take care in handling thin core laminates as they are easily damaged.
  • If the prepreg is not consumed within 48hrs after opening the vacuum package, it is recommended that the bags be resealed.
  • Material is available in both long and short grain. The grain direction is indicated on the label with an arrow.

 

Designing And Inner Layer Process

  • Please be careful when single ply of 1080, 1086, 1078 or 106 prepreg is designed to the dielectric layer.
  • Dimension stability is the same as Standard FR4 material.
  • Please check with your oxide vendor to make sure that our material is suitable with your oxide process. We recommend to control the peel strength with brown oxide copper over 2 Lb/in.
  • For unclad or single sided laminates to be used in multilayer, please brush unclad sides before use.

 

Prepreg Availability

E-Glass styles: 7628, 1506, 1500, 2113, 2313, 3313, 2116, 1080, 1086, 1078, 106, 1067 etc.

Prepreg Availability

PP Type Resin Content Press Thickness (mil) DK DF Remark
@ 1GHz @ 2GHz @ 5GHz @ 10GHz @ 1GHz @ 2GHz @ 5GHz @ 10GHz
7628 46% 8.00 4.16 4.11 4.11 4.06 0.014 0.014 0.014 0.016 Standard
7628 43% 7.60 4.26 4.20 4.20 4.15 0.013 0.013 0.013 0.015 Standard
1506 52% 7.40 3.98 3.92 3.90 3.85 0.015 0.015 0.016 0.017 Standard
2116 55% 5.20 3.93 3.87 3.87 3.80 0.015 0.015 0.016 0.017 Standard
2116 53% 4.90 3.98 3.92 3.90 3.85 0.015 0.015 0.016 0.017 Standard
2113 56% 4.00 3.87 3.82 3.82 3.77 0.015 0.015 0.016 0.017 Standard
1080 65% 3.20 3.68 3.63 3.63 3.58 0.017 0.017 0.018 0.019 Standard
1080 63% 3.00 3.73 3.69 3.65 3.60 0.017 0.017 0.018 0.019 Standard

① Press thickness test condition---Prepreg lamination size 18”*24”, Copper Foil---1oz/1oz, Flow---about 5%; ② Make laminated pre-preg to micro-section and measure the thickness with microscope; this thickness is used for resistance design calculation. ③ The thickness measured with micrometer is 0.2~0.4 mil larger than that measured with micro-section; and mainly used for total thickness design calculation.

Laminate Availablity

Thickness: 0.002” (0.05mm) to 0.200” (5mm), available in sheet or panel form Copper Foil: 1/4 to 12oz, HTE or RTF or DST DK values are for impedance design.

Laminate Availability

Core thk. (Inches) Stack-up Resin Content DK DF Remark
@ 1GHz @ 2GHz @ 5GHz @ 10GHz @ 1GHz @ 2GHz @ 5GHz @ 10GHz
0.002 1-106 70% 3.55 3.50 3.50 3.45 0.018 0.018 0.019 0.020 Standard
0.003 1-1080 63% 3.73 3.69 3.65 3.60 0.017 0.017 0.018 0.019 Standard
0.004 1-2116 44% 4.17 4.13 4.13 4.08 0.014 0.014 0.015 0.016 Standard
0.004 2-106 70% 3.55 3.50 3.50 3.45 0.018 0.018 0.019 0.020 2ply
0.005 1-2116 53% 3.98 3.92 3.90 3.85 0.015 0.015 0.016 0.017 Standard
0.006 1-1506 45% 4.16 4.11 4.11 4.06 0.014 0.014 0.014 0.016 Standard
0.007 1-7628 41% 4.27 4.23 4.23 4.18 0.013 0.013 0.013 0.015 Standard
0.008 1-7628 45% 4.16 4.11 4.11 4.06 0.014 0.014 0.014 0.016 Standard
0.008 2-2116 44% 4.17 4.13 4.13 4.08 0.014 0.014 0.015 0.016 2ply
0.010 2-2116 53% 3.98 3.92 3.90 3.85 0.015 0.015 0.016 0.017 Standard
0.012 2-1506 44% 4.17 4.13 4.13 4.08 0.014 0.014 0.014 0.016 Standard
0.014 2-7628 40% 4.29 4.25 4.25 4.20 0.013 0.013 0.013 0.015 Standard
0.016 2-7628 45% 4.16 4.11 4.11 4.06 0.014 0.014 0.014 0.016 Standard
0.028 4-7628 40% 4.29 4.25 4.25 4.20 0.013 0.013 0.013 0.015 Standard
0.036 5-7628 42% 4.26 4.20 4.20 4.15 0.013 0.013 0.013 0.015 Standard
0.045 6-7628 42% 4.35 4.30 4.22 4.22 0.013 0.013 0.013 0.015 Standard
0.049 7-7628 40% 4.26 4.20 4.20 4.15 0.013 0.013 0.013 0.015 Standard
0.059 8-7628 42% 4.26 4.20 4.20 4.15 0.013 0.013 0.013 0.015 Standard

Press Condition

1. Heating rate(Rise of Rate) of material [Material Temperature]
Programmable Press: 1.5-3.0℃/min (3~5℉/min).  Manual Press:3~6℃ /min (5~10℉/min)

2. Curing Temperature & Time: >50min at more than 170℃ (338℉)[Material Temperature]

3. Full Pressure : ≥250-280psi

4. Vacuuming should be continued until over 140℃ (284℉) [Material Temperature]  

5. Cold Press condition:  
Keep Plate @ Room Temperature by water, Pressure:100psi, Keep Time:60minutes

hot-start-cycle-vt-42.jpg hot-start-cycle-vt-42-manual.jpg adara-cedal-press-cycle-vt-42.jpg

Typical Drilling Parameters (φ0.3-1.0 mm)

Desmearing Process

Standard FR4 Desmear Process.

Downloads for VT-42